See all Blog Posts What is Metal Aging? Category: Metal Man Knows, Processes Posted: January 3, 2020 Metal aging is one of the most common ways to alter the properties of a metal alloy. While many metals may have their properties altered through heating and quenching or work hardening, some metal alloys are specifically formulated to be aged. Aging can alter the physical and aesthetic properties of an alloy to give it characteristics quite different than its unaged form. What is Metal Aging? Metal aging is a process used on solution heat-treated metal alloys that can be done artificially or happen naturally. Natural aging occurs throughout the life of the metal alloy. During the natural aging process, super-saturated alloying elements within the metal alloy form what are known as metal precipitates. These precipitates block dislocations in the metal, increasing the strength and hardness of a metal alloy while reducing its ductility. Artificial aging is a process that is used to accelerate the formation of precipitates in a solution heat-treated metal alloy to a rate that is much faster than the natural aging process. The artificial aging process is performed by elevating the temperature of the solution heat-treated metal alloy to a point below its recrystallisation temperature but high enough to speed up precipitate formation. Once the alloying element precipitates have become the correct size, the metal alloy is then cooled rapidly to prevent any further change in the metal precipitates. What Types of Metals Can Be Aged? There are many types of metal alloys that can be aged to alter their physical properties, as long as they are solution heat-treatable: Aluminium Stainless Steel Copper Alloys Other Metal Alloys Aluminium: The 2XXX, 6XXX, and 7XXX series of aluminium alloys are all ageable and many of their various forms derive their strength from artificial aging. One of the most common aged aluminium alloys is 6061-T6. It has magnesium silicide precipitates that block dislocations and increase its strength and hardness greatly in the -T6 form. Stainless steel: 17/10P, 17/4PH (commonly known as 630 in the UK) , and 17/7PH are a few common stainless steel alloys that have extremely high strengths and hardnesses when they are properly aged because of the metal alloy precipitates in their structures. Copper alloys: C17200 and C17300 are two copper-beryllium alloys that are frequently used in industry. Generally known for being soft and ductile, copper can be quite hard, strong, and brittle when the right additions of alloying elements are used with a proper aging technique. Other metal alloys: Titanium, nickel, and magnesium, as well as several other metals, can be aged if they have alloying elements in their chemical makeup that make them solution heat-treatable. Overaging One concern when aging a metal alloy, either naturally or artificially, is something known as overaging. This occurs when the precipitates change in size due to an aging process that is performed past the point of being beneficial to the application. This often results in reduced strength and hardness. Two common ways this happens is by welding or cold working a metal. Care should be taken to determine if a solution heat-treatable metal needs to be artificially aged again, following one of these two processes to ensure that the desired mechanical properties are still present. Metal Supermarkets Metal Supermarkets is the world’s largest small-quantity metal supplier with over 100 brick-and-mortar stores across the US, Canada, and United Kingdom. We are metal experts and have been providing quality customer service and products since 1985. At Metal Supermarkets, we supply a wide range of metals for a variety of applications. Our stock includes: mild steel, stainless steel, aluminium, tool steel, engineering steel, brass, bronze and copper. We carry a wide range of shapes including: bars, tubes, sheets and plates. We can cut metal to your exact specifications. Visit one of our 7 locations in the United Kingdom today. Share: Facebook Twitter LinkedIn E-Mail Related blog articles Considerations for Building a Floating Dock What is Rebar? What are Brinell and Rockwell Hardness Measurements?